Formation of New Texture ,in C-doped a：SiO2 after High Energy Xe Irradiation
-
Graphical Abstract
-
Abstract
Amorphous silicon-dioxide （a：SiO2） films were firstly implanted at room temperature （RT） with 120 keV C-ions to doses ranging from 5.0 × 10^16 to 8.6 × 10^17 ion/cm^2, and then the C-doped a：SiO2 films were irradiated at RT with 1 754 MeV Xe ions to 1.0 × 10^11 and 5.0 × 10^11 ion/cm^2, respectively. The information of new tex- ture formation in the C-doped SiO2 films after high-energy Xe ion irradiation was investigated using micro-FTIR measurements. The obtained results showed that Si--C, C--C, Si--O--C bonds as well as CO and CO2 molecules were formed in the C-doped a-SiO2 films after Xe ion irradiation. Furthermore, Xe-ion irradiation induced a plenteous formation of Si--C bonds in the high dose C-ion implanted a：SiO2 films. Compared with the C-implanted sampies without Xe-ion irradiation and the low dose C-implanted samples with Xe-ion irraddiation, the enhanced and plenty of Si--C bond formation implied that the phase of SiC structures may be produced by Xe-ion irradiation in the high dose C-ion implanted a：SiO2 films.
-
-
DownLoad: